Chloride Stress Corrosion Cracking & Relative resistance of Various Stainless Steel Grades

por Productos

CORROSION: Chloride Stress Corrosion Cracking

Definition:

The combination of tensile stress and a specific corrosive environment can crack stainless steels.  This mode of attack is termed stress corrosion cracking (SCC). The most common environmental exposure condition responsible for SCC of stainless steels is the presence of chlorides.  Although no stainless steel grade is totally immune to chloride SCC, the relative resistance of stainless steels varies substantially.

Influence of Alloy Composition:

The relative resistance to chloride SCC is dependant on the stainless steel family.  The austenitic family of stainless steels is the most susceptible.  The resistance of austenitic stainless steels to SCC is related to the nickel content of the steel. 

The most susceptible austenitic grades have nickel contents in the range of 8 to 10 wt%.  Therefore, standard grades such as 304/304L and 316/316L are very susceptible to this mode of attack.  Austenitic grades with relatively high nickel and molybdenum contents such as alloy 20, 904L, and the 6% molybdenum super austenitic grades have substantially better chloride SCC resistance.

The ferritic family of stainless steels, which includes grades such as type 430 and 444 are very resistant to chloride SCC.  The duplex stainless steel with their dual austenite/ferrite microstructures has a resistance that is in between that of the austenite and ferrite grades.

Corrosion Testing

The relative resistance of a stainless steel to chloride SCC is often quantified by the use of standard boiling salt solutions.  The following table summarizes the results of testing in boiling salt solutions of 26% NaCl (sodium chloride), 33% LiCl (lithium chloride), and 42% MgCl2 (magnesium chloride).  The boiling LiCl and MgCl2 test solutions are very aggressive relative to practical applications and only austenitic alloys with compositions that approach those of nickel-base alloys will routinely resist cracking in these test solutions.

Table 1: Relative chloride SCC resistance measured using fully immersed U-bend specimens in standard boiling salt solutions. (Taken from producer data)

Alloy

42% MgCl2

33% LiCl

26% NaCl

Austenitic SST

Type 304L (S30403)

SCC

SCC

SCC

Type 316L (S31603)

SCC

SCC

SCC

904L (N08904)

SCC

SCC

No Cracking

6% Mo SST

SCC

SCC

No Cracking

Alloy 20 (N08020)

SCC

No Cracking

No Cracking

Duplex SST

2205 (S32205)

SCC

No Cracking

No Cracking

255 (S32550)

SCC

No Cracking

2507 (32750)

SCC

No Cracking

Ferritic SST

439 (S43035)

No Cracking

No Cracking

No Cracking

444 (S44400)

No Cracking

No Cracking

No Cracking

 

Crack Appearance

The typical crack morphology for chloride stress corrosion cracking consists of branched transgranular cracks.  Figure 1 shows the cracking that occurred on a 6Mo super austenitic stainless steel  (N08367) exposed to 0.2% chlorides at 500 °F (260 °C)

Figure 1: Typical appearance of chloride stress corrosion cracking

Photo courtesy of TMR Stainless

Environmental Factors:

The environmental factors that increase the cracking susceptibility include higher temperatures, increased chloride content, lower pH, and higher levels of tensile stress.  Temperature is an important variable.  When stainless steels are fully immersed, it is rare to see chloride stress corrosion cracking at temperatures below 60 °C (150 °F). 

There is a synergistic relationship between dissolved oxygen and the chloride level.  If the oxygen level is reduced to the 0.01 to 0.1 ppm range, aqueous solutions containing low to moderate chloride levels are not likely to crack austenitic alloys, such as 304L and 316L.  The normal solubility of O2 in water at room to moderate temperatures (e.g. up to 140°F/60°C) is 4.5 to 8 ppm at atmospheric pressure.

In actual service environments, evaporation can produce local build-up of aggressive corrosive substances, such as chlorides and the H+ ions, resulting in conditions that are substantially more aggressive.  Under severe evaporative conditions, stainless steels can crack at temperatures well below the thresholds measured under conditions where there is full immersion.  Because of this, one must use caution when specifying materials for applications that involve the evaporation of chloride-bearing solutions on hot stainless steel surfaces.

The Materials Technology Institute (MTI) of the Chemical Process Industry has reviewed literature and collected case histories to define guidelines for the chloride SCC susceptibility of types 304L and 316L stainless steel in neutral water environments. 

Figure 2 shows the cracking threshold for 304L and 316L stainless steel as a function of temperature and chloride content.  The level of chlorides required to produce cracking is relatively low.  Failures have been reported in environments with as little as 10 ppm chlorides.  This is particularly true for environments having concentrating (evaporating) mechanisms such as wet/dry interfaces or a film of solution in immediate contact with a heat-rejecting surface.  In these situations, a few ppm of chlorides in the bulk solution can concentrate to hundreds of ppm in the area of evaporation.

Figure 2: Cracking threshold for 304 and 316 alloys exposed to near neutral chloride-bearing waters

The cracking threshold of a 6Mo super austenitic stainless steel (UNS N08367) immersed in oxygen-bearing neutral chloride solutions is shown in Figure 3.  The temperature thresholds are well above the 212°F (100°C) range, indicating that exposures to atmospheric boiling in neutral chloride solutions are very unlikely to produce cracking.

Figure 3: Cracking threshold for a 6Mo super austenitic steel ( UNS N08367) immersed in neutral NaCl solutions.

Courtesy of TMR Stainless

Swimming Pools

As was noted above, it is rare to see chloride stress corrosion cracking at temperatures below 60 °C (150 °F). Elevated load bearing applications in interior swimming pools are an exception to this rule and have a unique set of conditions.  For more information, please read, Successful Stainless Swimming Pool Design, Stainless steels for swimming pool building applications – selection, use and avoidance of stress corrosion cracking,  and Stainless Steel in Swimming Pool Buildings.

Additional References

There are numerous NACE papers and stainless steel producer brochures on this topic. Additionally, the following industry association brochures are suggested as general references.

Nickel Institute brochure No. 11 021 High Performance Stainless Steels

Nickel Institute brochure 16001 Practical Guidelines for the Fabrication of High Performance Austenitic Stainless Steels

International Molybdenum Association brochure Practical Guidelines for the Fabrication of Duplex Stainless Steelsh

 Source : SSINA per David A. Hartquist, counsel to SSINA.

El responsabilidad y propiedad de contenido nuevo

Por favor leer antes de escribir un comentario
Cada usuario posee y es responsable por el contenido que postee en el sitio de Great Plains Stainless, incluyendo la información de que dicho Usuario publique y ponga a disposición de otros usuarios para ver.

Representaciones y garantías.

Al postear contenido en nuestro sitio,, usted garantiza que:

  • Usted tiene derecho a presentar contenido;
  • La información es exacta;
  • La información no es confidencial;
  • La aplicación del contenido no viola ninguna legislación ni es restringida contractualmente por terceras partes;
  • Es únicamente su responsabilidad garantizar la exactitud de su perfil y contenido enviado y para actualizar esa información, según convenga.

Licencia y uso del contenido.

Para que usted comparta su información con otras personas, Great Plains necesita su permiso para reproducir su información a través de este sitio. Por lo tanto, en virtud de estos Términos y Condiciones, al enviar, publicar o mostrar cualquier contenido o en este Sitio, usted se compromete a conceder a Great Plains Stainless de todo el mundo, asignable derecho no exclusivo, sublicenciable y libre de regalías que nos permita copiar, distribuir, publicar, eliminar, retener y utilizar su contenido o información sin consentimiento adicional, notificación o compensación con el único propósito de permitir a Great Plains Stainless para ofrecerle sus servicios.

Además, con el objetivo de llegar a más personas y facilitar las conexiones, usted otorga Great Plains el derecho de compartir la información publicada en nuestro sitio con otros sitios con los que tenemos alianzas. La información publicada en nuestro sitio pueden convertirse en información pública en el momento de su distribución en otros sitios, a través de alertas de correo electrónico, canales RSS, motores de búsqueda, y otras herramientas de medios sociales.

Además, al presentar o publicar contenido en el sitio, usted se compromete a ofrecer a otros usuarios permiso para descargar y compartir el contenido de este sitio, siempre que correctamente atribuyan la obra al autor, no alterarlo de cualquier manera, y no copiar o utilizar la obra con fines comerciales.

Comunicación de usuario a usuario. El sitio incluye varios foros y blogs donde puedes publicar tus observaciones y comentarios sobre temas designados. Great Plains Stainless no puede garantizar que otros usuarios no utilicen las ideas y la información que se comparte. Por lo tanto, si usted tiene una idea o información que desea mantener confidencial y / o no desea que otros utilicen, no la publique en el Sitio.

Great Plains no es responsable por el mal uso de un Usuario o apropiación indebida de cualquier contenido o información que publique en cualquier foro, blog, y otras secciones del sitio.